Technische Specificaties Materialen (FDM)
PLA
PETG
TPU
ASA
PA6-GF
PAHT-CF
PPA-CF
PPS-CF
PC
PVA
PLA
Properties
Bambu Lab has tested the differing aspects in the performance of PLA Basic material, including physical, mechanical, and chemical properties. Typical values are listed as followed:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.24 g/cm³ |
| Melt Index | 210 °C, 2.16 kg | 23.2 ± 3.5 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 160 °C |
| Glass Transition Temperature | DSC, 10 °C/min | 60 °C |
| Crystallization Temperature | DSC, 10 °C/min | N / A |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 57 °C |
| HDT (1.8 MPa) | ISO 75 | 54 °C |
| HDT (0.45 MPa) | ISO 75 | 57 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 0.43% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 2580 ± 220 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 2060 ± 170 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 35 ± 4 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 31 ± 3 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 12.2 ± 1.8% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 7.5 ± 1.3% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 2750 ± 160 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 2370 ± 150 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 76 ± 5 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 59 ± 6 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 26.6 ± 2.8 kJ/m²; 7.9 ± 1.2 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 13.8 ± 0.9 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | PLA |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Not resistant |
| Resistance to Alkali | Not resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides |
| Odor of Combustion Products | Odorless |
PETG
Properties
Bambu Lab has tested PETG material for physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.28 g/cm³ |
| Melt Index | 210 °C, 2.16 kg | 28.2 ± 2.7 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 214 °C |
| Glass Transition Temperature | DSC, 10 °C/min | 66 °C |
| Crystallization Temperature | DSC, 10 °C/min | N / A |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 70 °C |
| HDT (1.8 MPa) | ISO 75 | 62 °C |
| HDT (0.45 MPa) | ISO 75 | 69 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 0.40% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 1810 ± 190 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 1540 ± 130 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 34 ± 4 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 23 ± 4 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 8.6 ± 1.2% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 5.1 ± 0.8% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 2050 ± 120 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 1810 ± 140 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 64 ± 3 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 48 ± 4 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 31.5 ± 2.2 kJ/m²; 6.2 ± 1.8 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 10.6 ± 1.2 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | PETG |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Not resistant |
| Resistance to Alkali | Not resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides |
| Odor of Combustion Products | Odorless |
TPU 95A HF
Properties
Bambu Lab has tested the differing aspects in the performance of TPU 95A HF material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.22 g/cm³ |
| Melt Index | 210 °C, 2.16 kg | 36.5 ± 2.6 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 183 °C |
| Glass Transition Temperature | DSC, 10 °C/min | N / A |
| Crystallization Temperature | DSC, 10 °C/min | N / A |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | N / A |
| HDT (1.8 MPa) | ISO 75 | N / A |
| HDT (0.45 MPa) | ISO 75 | N / A |
| Water Absorption (Saturated) | 25 °C, 55% RH | 1.08% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 9.8 ± 0.7 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 7.4 ± 0.6 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 27.3 ± 0.8 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 22.3 ± 0.6 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | > 650% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | > 480% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | N / A |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | N / A |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | N / A |
| Bending Strength (Z) | ISO 178, GB/T 9341 | N / A |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 123.2 kJ/m² |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 86.3 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | Thermoplastic polyurethane |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Not resistant |
| Resistance to Alkali | Not resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides, nitrogen oxides |
| Odor of Combustion Products | Pungent odor |
ASA
Properties
Bambu Lab has tested the differing aspects in the performance of ASA material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.05 g/cm³ |
| Melt Index | 260 °C, 2.16 kg | 7.0 ± 0.8 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 210 °C |
| Glass Transition Temperature | DSC, 10 °C/min | N / A |
| Crystallization Temperature | DSC, 10 °C/min | N / A |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 106 °C |
| HDT (1.8 MPa) | ISO 75 | 92 °C |
| HDT (0.45 MPa) | ISO 75 | 100 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 0.45% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 2450 ± 270 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 2120 ± 260 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 37 ± 3 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 31 ± 4 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 9.2 ± 1.4% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 4.6 ± 0.8% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 1920 ± 130 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 1650 ± 120 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 65 ± 5 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 40 ± 3 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 41.0 ± 2.3 kJ/m²; 19.6 ± 1.8 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 4.9 ± 0.6 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | Acrylonitrile – Styrene – Acrylate |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Resistant |
| Resistance to Alkali | Resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Not resistant to some kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides, nitrogen oxides |
| Odor of Combustion Products | Pungent odor |
PA6-GF
Properties
Bambu Lab has tested the differing aspects in the performance of PA6-GF material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.14 g/cm³ |
| Melt Index | 280 °C, 2.16 kg | 9.0 ± 0.8 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 219 °C |
| Glass Transition Temperature | DSC, 10 °C/min | 67 °C |
| Crystallization Temperature | DSC, 10 °C/min | 183 °C |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 210 °C |
| HDT (1.8 MPa) | ISO 75 | 158 °C |
| HDT (0.45 MPa) | ISO 75 | 182 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 2.56% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 2850 ± 260 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 1950 ± 210 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 75 ± 6 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 27 ± 5 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 3.9 ± 0.8% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 2.3 ± 0.7% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 3670 ± 140 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 2300 ± 120 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 120 ± 6 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 51 ± 5 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 27.2 ± 2.2 kJ/m²; 7.2 ± 2.3 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 4.1 ± 0.7 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | Nylon 6, glass fiber |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Not resistant |
| Resistance to Alkali | Not resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides, nitrogen oxides |
| Odor of Combustion Products | Pungent odor |
PAHT-CF
Properties
Bambu Lab has tested the differing aspects in the performance of PAHT-CF material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.06 g/cm³ |
| Melt Index | 280 °C, 2.16 kg | 14.4 ± 2.0 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 225 °C |
| Glass Transition Temperature | DSC, 10 °C/min | 70 °C |
| Crystallization Temperature | DSC, 10 °C/min | 140 °C |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 220 °C |
| HDT (1.8 MPa) | ISO 75 | 170 °C |
| HDT (0.45 MPa) | ISO 75 | 194 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 0.88% |
Mechanical Properties (Dry state)
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 3860 ± 230 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 2180 ± 130 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 92 ± 7 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 47 ± 5 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 8.4 ± 1.8% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 4.1 ± 1.2% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 4230 ± 210 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 1820 ± 170 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 125 ± 7 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 61 ± 5 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 57.5 ± 3.4 kJ/m²; 22.8 ± 1.8 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 13.3 ± 0.8 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | PA 12 and other long-chain PA, carbon fiber |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Not resistant |
| Resistance to Alkali | Not resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides, nitrogen oxides |
| Odor of Combustion Products | Pungent odor |
PPA-CF
Properties
Bambu Lab has tested the differing aspects in the performance of PPA-CF material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.25 g/cm³ |
| Melt Index | 280 °C, 2.16 kg | 8.4 ± 0.7 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 258 °C |
| Glass Transition Temperature | DSC, 10 °C/min | 85 °C |
| Crystallization Temperature | DSC, 10 °C/min | 178 °C |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 232 °C |
| HDT (1.8 MPa) | ISO 75 | 196 °C |
| HDT (0.45 MPa) | ISO 75 | 227 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 1.30% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 11800 ± 670 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 4300 ± 340 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 168 ± 4 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 57 ± 5 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 3.2 ± 0.4% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 0.9 ± 0.2% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 9860 ± 480 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 3240 ± 360 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 208 ± 6 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 63 ± 4 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 41.7 ± 2.8 kJ/m²; 6.5 ± 2.3 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 4.3 ± 0.4 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | Semi-aromatic Nylon, carbon fiber |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Better than general Nylon; resistant to weak acids, but not resistant to strong acids |
| Resistance to Alkali | Better than general Nylon; resistant to weak alkalis, but not resistant to strong alkalis |
| Resistance to Organic Solvent | Better than general Nylon; resistant to most kinds of organic solvents |
| Resistance to Oil and Grease | Better than general Nylon; resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides, nitrogen oxides, etc. |
| Odor of Combustion Products | Pungent odor |
PPS-CF
Properties
Bambu Lab has tested the differing aspects in the performance of PPS-CF material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.26 g/cm³ |
| Melt Index | 320 °C, 2.16 kg | 11.48 ± 1.23 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 284 °C |
| Glass Transition Temperature | DSC, 10 °C/min | 100 °C |
| Crystallization Temperature | DSC, 10 °C/min | 214 °C |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 268 °C |
| HDT (1.8 MPa) | ISO 75 | 235 °C |
| HDT (0.45 MPa) | ISO 75 | 264 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 0.05% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 8230 ± 270 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 2850 ± 160 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 87 ± 5 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 24 ± 3 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 1.2 ± 0.4% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 0.7 ± 0.3% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 7160 ± 280 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 2460 ± 190 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 142 ± 5 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 36 ± 4 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 27.8 ± 2.3 kJ/m²; 6.2 ± 1.6 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 2.8 ± 0.4 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | Polyphenylene sulfide (PPS), carbon fiber |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Resistant |
| Resistance to Alkali | Resistant |
| Resistance to Organic Solvent | Resistant |
| Resistance to Oil and Grease | Resistant |
| Flammability | Self-extinguishing when away from fire; flame-retardant |
| Thermal Decomposition and Oxidation Products | Hydrocarbons, water, carbon oxides, sulfur dioxide, sulfides |
| Odor of Thermal Decomposition and Oxidation Products | Characterized odor |
PC
Properties
Bambu Lab has tested the differing aspects in the performance of PC material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.20 g/cm³ |
| Melt Index | 260 °C, 2.16 kg | 32.2 ± 2.9 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 228 °C |
| Glass Transition Temperature | DSC, 10 °C/min | 145 °C |
| Crystallization Temperature | DSC, 10 °C/min | N/A |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | 119 °C |
| HDT (1.8 MPa) | ISO 75 | 117 °C |
| HDT (0.45 MPa) | ISO 75 | 112 °C |
| Water Absorption (Saturated) | 25 °C, 55% RH | 0.25% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | 2110 ± 40 MPa |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | 1450 ± 60 MPa |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | 55 ± 4 MPa |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | 34 ± 3 MPa |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | 3.8 ± 0.3% |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | 2.1 ± 0.4% |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | 2310 ± 70 MPa |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | 1620 ± 80 MPa |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | 108 ± 4 MPa |
| Bending Strength (Z) | ISO 178, GB/T 9341 | 55 ± 2 MPa |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | 34.8 ± 2.1 kJ/m²; 7.5 ± 1.3 kJ/m² (notched) |
| Impact Strength (Z) | ISO 179, GB/T 1043 | 9.0 ± 0.4 kJ/m² |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | Polycarbonate (PC) |
| Skin Hazards | No hazard |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Insoluble in water |
| Resistance to Acid | Not resistant |
| Resistance to Alkali | Not resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides |
| Odor of Combustion Products | Light phenol-flavored odor |
PVA
Properties
Bambu Lab has tested the differing aspects in the performance of PVA material, including physical, mechanical, and chemical properties. Typical values are listed below:
Physical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Density | ISO 1183 | 1.27 g/cm³ |
| Melt Index | 210 °C, 2.16 kg | 7.2 ± 1.1 g/10 min |
| Melting Temperature | DSC, 10 °C/min | 202 °C |
| Glass Transition Temperature | DSC, 10 °C/min | N/A |
| Crystallization Temperature | DSC, 10 °C/min | N/A |
| Vicat Softening Temperature | ISO 306, GB/T 1633 | N/A |
| HDT (1.8 MPa) | ISO 75 | N/A |
| HDT (0.45 MPa) | ISO 75 | N/A |
| Water Absorption (Saturated) | 25 °C, 55% RH | 6.25% |
Mechanical Properties
| Subject | Testing Method | Data |
|---|---|---|
| Young’s Modulus (X-Y) | ISO 527, GB/T 1040 | N/A |
| Young’s Modulus (Z) | ISO 527, GB/T 1040 | N/A |
| Tensile Strength (X-Y) | ISO 527, GB/T 1040 | N/A |
| Tensile Strength (Z) | ISO 527, GB/T 1040 | N/A |
| Elongation at Break (X-Y) | ISO 527, GB/T 1040 | N/A |
| Elongation at Break (Z) | ISO 527, GB/T 1040 | N/A |
| Bending Modulus (X-Y) | ISO 178, GB/T 9341 | N/A |
| Bending Modulus (Z) | ISO 178, GB/T 9341 | N/A |
| Bending Strength (X-Y) | ISO 178, GB/T 9341 | N/A |
| Bending Strength (Z) | ISO 178, GB/T 9341 | N/A |
| Impact Strength (X-Y) | ISO 179, GB/T 1043 | N/A |
| Impact Strength (Z) | ISO 179, GB/T 1043 | N/A |
Other Physical and Chemical Properties
| Subject | Data |
|---|---|
| Odor | Odorless |
| Composition | Polyvinyl Alcohol (PVA) |
| Skin Hazards | Not available |
| Chemical Stability | Stable under normal storage and handling conditions |
| Solubility | Soluble in water |
| Resistance to Acid | Not resistant |
| Resistance to Alkali | Not resistant |
| Resistance to Organic Solvent | Not resistant to some organic solvents |
| Resistance to Oil and Grease | Resistant to most kinds of oil and grease |
| Flammability | Flammable |
| Combustion Products | Water, carbon oxides, etc. |
| Odor of Combustion Products | Light pungent odor |